Selenium Nanoparticle Activity against S. mutans Biofilms as a Potential Treatment Alternative for Periodontitis

Abstract

The disruption of periodontal biofilms and prevailing antimicrobial resistance issues continue to pose a great challenge to the treatment of periodontitis. Here, we report on selenium nanoparticles (SeNPs) as a treatment alternative for periodontitis by determining their antibiofilm activity against <i>S. mutans</i> biofilms and the potential role of particle size in disrupting biofilms. SeNPs were synthesised via a reduction reaction. Various physicochemical characterisations were conducted on the NPs, including size and shape. The microbroth dilution method was used to conduct the biofilm and antibiofilm assay against <i>S. mutans</i>, which was analysed by absorbance. SeNPs displayed hydrodynamic sizes as low as 46 ± 4 nm at a volume ratio of 1:5 (sodium selenite/ascorbic acid) with good monodispersity and stability. Hydrodynamic sizes of SeNPs after resuspension in tryptic soy broth supplemented with 2.5% sucrose (TSB + 2.5% suc.) and incubated at 37 °C for 24 h, ranged from 112 to 263 nm, while the zeta potential values increased to greater than -11 mV. The biofilm assay indicated that <i>S. mutans</i> are weakly adherent, bordering on moderately adherent biofilm producers. The minimum biofilm inhibitory concentration (MBIC) was identified at 500 µg/mL. At a 1000 µg/mL concentration, SeNPs were able to inhibit <i>S. mutan</i> biofilms up to 99.87 ± 2.41% at a volume ratio of 1:1. No correlation was found between antibiofilm activity and particle size; however, antibiofilm activity was proven to be concentration-dependant. SeNPs demonstrate antibiofilm activity and may be useful for further development in treating periodontitis.