Production and characterization of pulp and paper from flax straw

Abstract

Flax (Linum usitatissimum) is a bast fiber plant known for its long fibers, making it an excellent source of pulp for paper production. In Ethiopia, flax is primarily cultivated for oil, with the residual straw utilized for papermaking. This study focuses on pulping flax straw using the Kraft process and investigates its chemical composition, proximate analysis, and morphological properties. The proximate analysis revealed an ash content of 4.13% and moisture content of 11%. Chemical composition analysis showed cellulose at 51.34%, hemicellulose at 25.20%, lignin at 14.12%, ash at 4.13%, and extractives at 5.21%. The morphological properties included a fiber length of 1.41 mm, diameter of 16.78 μm, lumen width of 9.45 μm, and cell wall thickness of 3.77 μm. Flax straw exhibited an acceptable Runkel ratio (0.8) and flexibility coefficient (56.32), placing it within the range of non-wood fibers. SEM analysis of the pulp's morphology was conducted to assess fiber structure, including the presence of cracks. Pulp quality and length are directly linked to paper strength. Various pulping conditions were studied using a full-factorial design, with optimum conditions being 10% alkaline, 131.74°C, and 120 min of cooking time, yielding a pulp with a Kappa number of 10.45 and a yield of 40.56%. The resulting paper demonstrated standard tensile, tearing, and burst strengths, indicating that flax straw is a promising raw material for paper production.