Humidity sensing using Zn(1.6 − x)Na0.4CuxTiO4 spinel nanostructures

Abstract

Abstract In this paper, we present a humidity sensing material based on nanostructured Zn (1.6 − x) Na 0.4 Cu x TiO 4 spinel to enhance optical and sensitivity performance. Nano-porous of Zn (1.6 − x) Na 0.4 Cu x TiO 4 spinel were synthesized using sol gel reactions and calcined at 700 °C. The nanostructures of Zn (1.6 − x) Na 0.4 Cu x TiO 4 spinel underwent thorough characterization through multiple techniques. X-ray diffractometry (XRD) coupled with Rietveld refinement using FullProf software, transmission electron microscopy (TEM), Raman Spectroscopy, and optical analysis were employed to assess various aspects of the nanostructures. These techniques were utilized to determine the phase composition, particle size distribution, chemical bonding, and the tunable band gap of the nanostructures. The X-ray diffraction (XRD) analysis of Zn (1.6 − x) Na 0.4 Cu x TiO 4 samples revealed well-defined and prominent peaks, indicating a highly crystalline cubic spinel structure. The lattice parameter was decreased from 8.4401 to 8.4212 Å with increasing Cu content from 0 to 1.2 mol%. UV–visible diffuse reflectance spectra were employed to investigate the optical characteristics of copper-doped Zn 1.6 Na 0.4 TiO 4 . The applicability of Cu@NaZT spinel nanostructures in humidity sensors was evaluated at ambient conditions. The fabricated sensor was investigated in a wide span of humidity (11–97%). The examined sensor demonstrates a low hysteresis, excellent repeatability, fast response and recovery. The response and recovery times were estimated to be 20 s and 6 s respectively. The highest sensitivity was achieved at 200 Hz. The proposed sensor can be coupled easily with electronic devices as the humidity–impedance relationship is linear.