Efficient Oxygen Evolution Reaction Performance of In Situ Hydrothermally Grown Cobalt–Nickel Layered Double Hydroxide on Nickel Foam

Abstract

CoNi layered double hydroxides (CoNiLDHs) were successfully synthesized on nickel foam (NF) using a hydrothermal method. X-ray diffraction (XRD) analysis confirmed the formation of a well-defined hydrotalcite-like phase, including a strong (003) peak, indicating layered stacking. Scanning electron microscopy (SEM) revealed a 3D hierarchical nanosheet structure resembling flower-like arrays, which was further supported by EDS mapping showing a uniform distribution of Co, Ni, and O. Electrochemical studies demonstrated excellent OER activity, with a low overpotential of 188 mV at 10 mA/cm2 and a Tafel slope of 97.48 mV/dec, inferring rapid reaction kinetics. Furthermore, the material exhibited a significant electrochemical surface area (ECSA) compared to bare NF. Chronoamperometry over 24 h confirmed the operational durability catalyst, stabilizing around 7–8 mA/cm2, validating its potential as a cost-effective and efficient OER electrocatalyst in alkaline media.