Effect of sintering time on microstructure and optical properties of yttria-partially stabilized monolithic zirconia

Abstract

To evaluate the impact of speed sintering on the microstructure and optical properties of 3 and 5 mol% yttria-partially stabilized monolithic zirconias. 120 plate-shaped zirconia specimens (10x10x 0.4 mm) were prepared from three commercial 5 mol% yttria-partially stabilized zirconia blocks (5Y-PSZs); Katana UTML (Kuraray Noritake), Cercon xtML (Dentsply Sirona), and Zolid FX white (Amann Girrbach), and two commercial 3 mol% yttria-partially stabilized zirconia blocks (3Y-PSZs); Lava Plus (3 M ESPE) and InCoris (Sirona, GmbH). Specimens were either conventional sintered (CS) using a 7-hour program or speed sintered (SS) using a quick 90-minute program. The microstructure was inspected with a scanning electron microscope (SEM), and phase fractions were detected using x-ray diffraction analysis (XRD). Translucency (TP00), and contrast ratio (CR) were obtained using a spectrophotometer (VITA Easyshade V). Color difference (ΔE00) between both sintering processes was calculated with the CIEDE2000 formula. ΔE00 up to 1.8 was set as the acceptability threshold. Data were analyzed using two-way ANOVA, Krusakll-Wallis, and Mann-Whitney U tests. (n = 12, α = .05). Grain size was significantly decreased after SS for all tested materials (P < .0001). The average grain sizes of 5Y-PSZs were significantly larger than those of 3Y-PSZs. The atomic structure, microstructure, and transparency of CS and SS were all affected by the amount of yttria, the size of the crystals, and tetragonality. SS significantly reduced TP00 (F = 7135.95, P < 0.0001) and increased CR (F = 453.21, P < 0.0001). The CS Katana presented the highest TP00 and lowest CR value. ΔE00 between the CS and SS groups were clinically acceptable except for Lava, which had values above the set threshold (1.89). SS altered the grain size and internal structure of the tested materials, which was reflected in translucency.