Ag doped TiO2 anchored on metal free g-C3N4 for enhanced solar light activated photodegradation of a dye

Abstract

Heterogeneous semiconductor photocatalysis has attracted researcher's attention in wastewater treatment owing to the improved surface area, optical properties, and charge transfer rate for boosted degradation of organic pollutants. Thus, the g-C 3 N 4 /Ag/TiO 2 was prepared following a hydrothermal route for the degradation of azo dye tartrazine (TA) used as a food colourant under solar light. Before application, the composite and pristine materials were interrogated for physicochemical and structural properties using SEM, TEM, EDS, XPS, XRD, UV–vis DRS, PL, BET, Raman, and FTIR spectroscopy. The PL and electrochemical analysis revealed that the CNAT composite had a high charge transfer rate that was coupled with low charge carrier complexation. The degradation efficiency of 91 % was realized in 180 min and the rate of pseudo-first-order kinetics of 0.01143 min −1 was obtained. The CNAT catalyst also displayed high removal efficiency towards a cocktail of naproxen (NPX) and TA. The improved removal efficiencies stem from increased visible usage, reduced charge carrier compounding, and formation of Z-scheme heterojunction with high redox capabilities. The total organic carbon removal reached 95 % while CNAT showed high convincing stability even after four cycles. Given the above results, the hydrothermally prepared composite catalyst can be extended to other organic pollutants such as pharmaceuticals, pesticides, and reduction of inorganics. • CNAT with the mixture of (TA and NPX) had 98 % TA and 40 % NPX degradation efficiency after synthesized by hydrothermal method. • Anatase CNAT composite was stable after four cycles. • Synthesized composite had high degradation efficiency. • Mineralization of TA and NPX, and degradation pathway was proposed.